Study and Application of Removing Oilwell Barium Sulphate through Complexing Method
-
摘要: 以二乙烯三胺五乙酸(DTPA)为螯合剂主剂,配以氢氧化钾中和至pH值为13,并添加一定量的无机盐,对重晶石粉末进行溶出研究。结果表明,在DTPA质量分数一定的情况下,由于溶液黏度影响,钾盐的助溶效果为钠盐的2倍;随着无机盐质量分数的增加,碳酸钾、氟化钾和氯化钾对重晶石的助溶效果相应增加,碳酸钾添加量为10%时,溶出率达到最高的47.79%;反应4 h时,由于重晶石结块导致反应面积增大,碳酸钾的助溶效果比氟化钾高10.56%;反应12 h时,反应趋于完全,由于盐效应影响反应终点,氟化钾的助溶效果比碳酸钾高12.39%;对DTPABa3-离子进行了计算机模拟,得到了其稳定构象,并分析了钡离子络合常数低的原因;最终将该螯合剂应用于某堵塞油井,并对返排液中的无机盐组分、硫酸盐沉淀组分进行了XRD分析,并在沉淀中检测出钡元素,证明油井解堵成功,应用良好。Abstract: The chelating agent used was mainly composed of diethylene triamine pentacetic acid (DTPA). It was neutralized with KOH until the pH was 13, and then treated with a certain amount of inorganic salts. This solution was used to dissolve out barite powders. The experimental results showed that, at a certain mass ratio of DTPA, the efficiency of potassium salts as solubilizing agent was 2 times of that of sodium salts due to the effect of the solution viscosity. Increasing the mass ratio of the inorganic salt, the efficiencies of potassium carbonate, potassium fluoride and potassium chloride as solubilizing agents in dissolving barite were correspondingly enhanced. At 10% of potassium carbonate, 47.79% of barite was dissolved. After 4 h of reaction, the conglomeration of barite led to an increase in reaction area, increasing the solubilizing efficiency of potassium carbonate to a value that was 10.56% higher than that of potassium fluoride. After reacting for 12 h, the reaction tended to complete, the solubilizing efficiency of potassium fluoride was instead higher than that of the potassium carbonateby 12.39% because of the salt effect on the reaction endpoint. The steady configuration of the DTPABa3-ions was obtained through computerized simulation, and the cause of low complexation constant of barium ions was analyzed. A chelating agent was chosen based on the study and was used on a well blocked with barite. The flowback fluid was analyzed for inorganic salts and precipitated sulphate using XRD. Barium was found in the precipitates, indicating that the well was successfully unblocked.
-
Key words:
- DTPA /
- Barite /
- Complex /
- Inorganic salt /
- Oilwell block removal
-
[1] 林枫,由福昌,王胜翔,等.加重钻井液防重晶石沉降技术[J].钻井液与完井液,2015,32(3):27-29.LIN Feng,YOU Fuchang,WANG Shengxiang,et al.Barite removal technology of heavy drilling fluid[J].Drilling Fluid &Completion Fluid,2015,32(3):27-29. [2] 李海波,张舰.油田防垢技术及其应用进展[J].化学工业与工程技术,2012,33(4):40-43.LI Haibo,ZHANG Jian.Oilfield inhibition technology and application progress[J].Journal of Chemical lndustry and Engineering,2012,33(4):40-43. [3] 常启新,李娟,苏克松,等.DTPA清除油田钡锶垢的影响因素研究[J].石油化工腐蚀与防护,2009,26(1):28-30.CHANG Qixin,LI Juan,SU Kesong,et al.Study on impact factor of barium strontium fouling removal in oil field by DTPA inhibitor[J].Corrosion and Protection in Petrochemical Industry,2009,26(1):28-30. [4] 刘峰,范白涛,刘宝生,等.重晶石解堵工艺技术在科学探索井储层改造中的应用[J].钻井液与完井液,2013,30(3):54-56.LIU Feng,FAN Baitao,LIU Baosheng,et al.Barite plugging technology to explore the application of reservoir in Science[J].Drilling Fluid &Completion Fluid,2013,30(3):54-56. [5] 付美龙.DTPA溶解硫酸钡垢的实验研究[J].钻采工艺,1999,22(1):53-55.FU Meilong.Laboratory study on DTPA dissolving BaSO 4 scale[J].Drilling and Production Technology,1999,22(1):53-55. [6] 郭丽梅,谭国锋,郭燕.油田硫酸盐垢除垢实验研究[J].杭州化工,2010,40(4):17-18.GUO Limei,TAN Guofeng,GUO Yan.Study on scaling of sulfate scale in oilfield[J].Hangzhou Chemical Industry,2010,40(4):17-18. [7] 王文华,赵林,阎波.离子对水结构的影响[J].化学通报,2010,(6):491-497.WANG Wenhua,ZHAO Lin,YAN Bo.Effect of ions on water structure[J].Chemistry,2010,(6):491-497. [8] 徐博,王凤武.初探无机化合物的颜色[J].淮南师范学院学报,2007,9(5):17-20.XU Bo,WANG Fengwu.Color of inorganic compounds[J].Journal of Huainan Normal University,2007,9(5):17-20.
点击查看大图
计量
- 文章访问数: 547
- HTML全文浏览量: 154
- PDF下载量: 155
- 被引次数: 0