A Well Cementing Slurry Used in Arctic Permafrost
-
摘要: 近年来,北极地区石油勘探开发进度明显加快,市场前景良好。针对北极永久冻土层最低温度达-9℃的超低温以及该地区作业时间宝贵的问题,要求水泥浆体系在负温环境下候凝时间短且24 h有强度发展。通过研发低温胶凝材料C-SE8和缓凝剂H10S,并复配G级油井水泥和其他添加剂,分别用淡水、海水和14% NaCl溶液配制超低温水泥浆体系。评价结果表明,密度为1.50 g/cm3的水泥浆在-10℃下的24 h抗压强度可达3.6 MPa以上,密度为1.90 g/cm3的水泥浆在-10℃下的24 h抗压强度可达6.8 MPa以上;该体系适用温度为-10℃~30℃,浆体具有良好的流变性能,且稠化时间易调整,满足北极永久冻土层固井施工要求。Abstract: Petroleum exploration and development in the Arctic area in recent years has been accelerating. Well cementing operation in this area has long been facing with ultra-low temperature (-9 ℃) and the precious time available for operation; the cement slurry is required to have strength development in 24 hours at temperatures below zero. Using a self-developed low temperature gelling agent C-SE8 and a self-developed retarder H10S, several ultra-low temperature cement slurries were formulated with class G cement and other additives in fresh water, sea water and 14% NaCl solution. Evaluation of the cement slurries showed that a cement slurry of 1.50 g/cm3 had 24 h compressive strength of at least 3.6 MPa at -10 ℃; another cement slurry of 1.90 g/cm3 had 24 h compressive strength of at least 6.8 MPa at -10 ℃. The working temperatures of the cement slurries were between -10 ℃ and 30 ℃. The cement slurries had good rheology, and the thickening time can be easily adjusted, making them suitable for well cementing in arctic permafrost.
-
Key words:
- Ultra-low temperature /
- Permafrost /
- Compressive strength /
- Thickening time
-
[1] MORRIS E F. Evaluation of cement systems for permafrost[C]//Annual Meeting of the American Institute of Mining, Metallurgical, and Petroleum Engineers.SPE 2824, 1970. [2] WATSON P, RICHARD B, THOMAS P ANDYR. An innovative approach to development drilling in the deepwater Gulf of Mexico[J].World Oil, 2004, 225(1):41-48. [3] 王彪, 陈彬, 阳文学, 等. 深水表层固井水泥浆体系应用现状及发展方向[J]. 石油钻采工艺,2015,37(1):107-110.WANG Biao, CHEN Bin, YANG Wenxue, et al. Application status and development direction of cement slurry system in deepwatersurface[J].Oil Drilling & Production Technology, 2015, 37(1):107-110. [4] 王建东, 屈建省, 高永会. 国外深水固井水泥浆技术综述[J]. 钻井液与完井液, 2005, 22(6):54-56, 61. WANG Jiandong, QU Jiansheng, GAOYonghui.The review of deep sea cementing slurry technology abroad[J]. Drilling Fluid & Completion Fluid, 2005, 22(6):54-56, 61. [5] 席方柱, 屈建省, 吕光明, 等. 深水低温固井水泥浆的研究[J]. 石油钻采工艺, 2010, 32(1):40-44.XI Fangzhu, QU Jiansheng, LYU Guangming, et al. Study of deepwater low-temperature cement slurry[J]. Oil Drilling & Production Technology, 2010, 32(1):40-44. [6] 步玉环, 侯献海, 郭胜来. 低温固井水泥浆体系的室内研究[J]. 钻井液与完井液, 2016, 33(1):79-83.BU Yuhuan, HOU Xianhai, GUO Shenglai. Study on low temperature cementing slurry[J]. Drilling Fluid & Completion Fluid, 2016, 33(1):79-83. [7] 赵琥, 邱超, 宋茂林, 等. 深水固井低温水泥外加剂的开发及应用[J]. 石油钻探技术, 2012, 40(4):72-75.ZHAO Hu, QIU Chao, SONG Maolin, et al. Development and application of additive in deepwater cementing[J]. Petroleum Drilling Techniques, 2012, 40(4):72-75. [8] 王晓亮, 许明标, 王清顺, 等. 深水表层固井硅酸盐水泥浆体系研究[J]. 石油钻探技术, 2010, 38(6):11-14.WANG Xiaolian, XU Mingbiao, WANG Qingshun, et al. Research on G-class portland cementing slurry in surface casing in deep water[J]. Petroleum Drilling Techniques, 2010, 38(6):11-14. [9] 冯颖韬, 宋茂林, 张浩, 等. 深水固井液体减轻低密度水泥浆体系[J]. 钻井液与完井液, 2017, 34(4):80-84.FENG Yingtao, SONG Maolin, ZHANG Hao, et al. Liquid cementing fluid reduced lightened deep water lightweight cement slurry[J]. Drilling Fluid & Completion Fluid, 2017, 34(4):80-84. [10] American Petroleum Institute (API).API RP 10B-2-2013 Recommended practice for testing well cements[S].2019. [11] 田群山, 张永海, 吴天师, 等. 南祁连冻土层固井技术研究与应用[J]. 西部探矿工程, 2012, 24(9):57-58.TIAN Qunshan, ZHANG Yonghai, WU Tianshi, et al. The research and application of cementing technology in the frozen soil of Nanqilian[J]. Western Exploration Engineering, 2012, 24(9):57-58.
点击查看大图
计量
- 文章访问数: 648
- HTML全文浏览量: 201
- PDF下载量: 66
- 被引次数: 0