A Magnesium Oxychloride Cement Slurry for Controlling Loss of Oil Base Drilling Fluids
-
摘要: 氯氧镁水泥具有优良的机械和热性能,常作为工业地板、防火、砂轮和墙体保温材料。针对常规水泥浆存在的抗侵污能力和酸溶性差,无法处理油基钻井液恶性漏失问题。利用氯氧镁水泥硬化体系的多元结晶相,采用DISP-S作为分散剂,DOT和Atmp复配作为缓凝剂,对氯氧镁水泥体系进行了优化,设计了一种可应用于油基钻井液大型漏失的堵漏水泥浆体系。实验结果表明,该堵漏水泥浆的密度为1.76 g/cm3,沉降稳定性良好,自由水含量几乎为0,失水量小于40 mL,在60℃下的稠化时间可达230 min,在中低温范围内水泥石的抗压强度均在30 MPa以上,侵入油基钻井液的水泥石仍然具备一定的力学性能,并且能在浓盐酸中完全溶解。Abstract: Magnesium oxychloride cement has excellent mechanical and thermal performance and is widely used in industrial flooring, fire control, grind wheel making and wall insulation. Conventional cement has some disadvantages as well cementing material such as poor contamination resistance, poor acid solubility and inability to deal with severe mud losses. To resolve these problems, a magnesium oxychloride cement slurry was developed using DISP-S as dispersant, and DOT and Atmp compound as retarder. The set magnesium oxychloride cement has polycrystalline phase in it and the slurry is able to deal with severe loss of oil base mud. Laboratory experimental results showed that a magnesium oxychloride cement slurry of 1.76 g/cm3 has very good settling stability, zero free water, filtration rate of less than 40 mL, thickening time of 230 min at 60℃, and set cement with compressive strength of greater than 30 MPa in intermediate and low temperatures. The set cement, even mixed with some invading oil base mud, still maintains certain level of mechanical properties, and is able to dissolve completely in concentrated hydrochloric acid.
-
[1] 马聪, 高义, 周希圣, 等. 缓凝剂对改性磷铝酸盐水泥水化的作用机理[J]. 哈尔滨工程大学学报, 2017, 38(1):43-47.MA Cong, GAO Yi, ZHOU Xisheng, et al.Influence mechanism of retarders on the hydration of modified phosphoaluminate cement[J].Journal of Harbin Engineering University, 2017, 38(1):43-47. [2] 严育通, 景燕, 马军. 氯氧镁水泥的研究进展[J]. 盐湖研究, 2008, 16(1):60-66.YAN Yutong, JING yan, MA Jun.Research progress of magnesium oxychloride cement[J].Journal of Salt Lake Research, 2008, 16(1):60-66. [3] 袁中涛, 杨谋, 李晓春, 等. 油基钻井液与水泥浆接触污染内因探讨[J]. 石油钻采工艺, 2017, 39(5):574-579.YUAN Zhongtao, YANG Mou, LI Xiaochun, et al. Discussion on the internal causes of contact contamination between oil-base drilling fluid and cement slurry[J].Oil Drilling & Production Technology, 2017, 39(5):574-579. [4] 李早元, 辜涛, 郭小阳, 等. 油基钻井液对水泥浆性能的影响及其机理[J]. 天然气工业, 2015, 35(8):63-68.LI Zaoyuan, GU Tao, GUO Xiaoyang, et al.Effects of oil-based drilling fluid on cement slurry performance and its mechanisms[J].Natural Gas Industry, 2015, 35(8):63-68. [5] 李炎. 耐高温聚合物降滤失剂AAS的研制与性能评价[J]. 石油钻探技术, 2015, 43(4):96-101.LI Yan.Development and performance evaluation of the high temperature resistant polymer fluid loss agent AAS[J].Petroleum Drilling Techniques, 2015, 43(4):96-101. [6] 张翠苗, 杨红建, 马学景. 氯氧镁水泥的研究进展[J]. 硅酸盐通报, 2014, 33(1):117-121.ZHANG Cuimiao, YANG Hongjian, MA Xuejing. Research progress of magnesium oxychloride cement[J]. Bulletin of the Chinese Ceramic Society, 2014, 33(1):117-121. [7] 余红发. 氯氧镁水泥及其应用[M]. 北京:中国建材工业出版社, 1993. YU Hongfa.Magnesium oxychloride cement and its application[M].Beijing:China Building Materials Industry Press, 1993. [8] BOUR D L, VINSON E F, TOTTEN P L.Low-density acid-removable cement as a solution for lost circulation across producing formations[J].SPE 25543, 1993:3-6. [9] BRIAN SEYMOUR, ASHOK SANTRA.Detailed laboratory investigation of acid soluble cements as solution for lost circulation across the producing zones[J]. SPE 166804, 2013:1-9. [10] ASHOK SANTR A, FENG LIANG, ROCKY FITZGERALD.Sorel cement for hpht downhole applications[C]//SPE International Symposium on Oilfield Chemistry, 2009, SPE 121102. [11] BILINSIK H, MATROVIC B, MAZURANIC C, et al. The fomation of magnesium oxychloride phases in the system MgO-MgCl2-H2O and NaOH-MgCl2-H2O[J].J Am Ceram Soc, 1984, 67(4):266-269. [12] VED E I, ZHAROV E F, PHONG H V. Mechanism of magnesium oxychloride formation during the hardening of agnesiun oxychloride cement[J].Zh Prikl Khim, 1976, 49(10):2154-2158. [13] 赵友星. 镁硅复合材料的制备及吸附性能的研究[D]. 青岛:中国海洋大学, 2011. ZHAO Youxing.Synthesis and sorption properties of the porous magnesian/silica materials[D].Qingdao:Ocean University of China, 2011. [14] BRIAN SEYMOUR, ASHOK SANTRA.Detailed laboratory investigation of acid soluble cements as solution for lost circulation across the producing zones[C]//SPE/IADC Middle East Drilling Technology Conference & Exhibition:conference proceedings:"Delivering Future Energy Through People, Technology, and Standards":7-9 October, 2013, Madinat Jumeirah, Dubai, UAE 2013:1-9. [15] LUKE K, SOUCY K.Test method to optimize acidsoluble cement for unconventional gas completions[C].//Canadian International Petroleum Conference SPE Gas Technology Symposium, 20090708:1-11. [16] REPETTOC, MORONI N PILIA. Successful application of acid-soluble plugs in openhole slottedliner completion[C]//SPE Oil & Gas India Conference & Exhibition, 2010:1-9. [17] HARDER C, CARPENTERAND R, WILSON W, et al. Surfactant/cement blends improve plugging operations in oil-base muds[C]//IADC/SPE Drilling Conference, 18-21 February, New Orleans, 1992. [18] LUKE K, SOUCY K.Test method to optimize acidsoluble cement for unconventional gas completions[J]. SPE 114759, 2008:1-11. [19] 钟声. 油基钻井液下水泥浆抗污剂的研究与应用[J]. 钻井液与完井液, 2016, 33(5):84-87.ZHONG Sheng. Study and application of anticontamination agent for cement slurry in wells drilled with oil base drilling fluids[J].Drilling Fluid & Completion Fluid, 2016, 33(5):84-87. [20] SPE International Oil & Gas Conference and Exhibition in China.Technology of plugging long-interval high-pressure channeling wells by cement with overburden pressure during curing[C].//Sustainable Growth for Oil and Gas, 2006:1-5. [21] 王在明, 吴艳, 朱宽亮, 等. 井壁强化与堵漏双作用可钻水泥实验研究[J]. 钻井液与完井液, 2017, 34(6):52-55.WANG Zaiming,WU Yan,ZHU Kuanliang et al. Experimental Study on Drillable Set Cement Capable of Strengthening Borehole Wall and Controlling Lost Circulation[J].Drilling Fluid & Completion Fluid, 2017, 34(6):52-55. [22] 杨广国, 陶谦, 高元, 等. 高温高压气井复合型水泥浆体系研究与应用[J]. 科学技术与工程,2016,16(20):151-155.YANG Guangguo, TAO Qian, GAO Yuan, et al. Research and application of high temperature high pressure gas well complex cement slurry[J].Science Technology and Engineering, 2016, 16(20):151-155. [23] 马勇, 郭小阳, 姚坤全, 等. 钻井液与水泥浆化学不兼容原因初探[J]. 钻井液与完井液, 2010, 27(6):46-48.MA Yong, GUO Xiaoyang, YAO Kunquan, et al. Research of chemical contamination between drilling fluids and slurry[J].Drilling Fluid & Completion Fluid, 2010, 27(6):46-48.
点击查看大图
计量
- 文章访问数: 555
- HTML全文浏览量: 127
- PDF下载量: 162
- 被引次数: 0