Preparation and Analyses of Nano SiO2 Plugging Agent Modified with Silane Coupling Agent
-
摘要: 以正硅酸乙酯(TEOS)为硅源,氨水为催化剂,水为促进剂,苯乙胺丙基三甲氧基硅烷为表面改性剂,采用溶胶-凝胶法,制备了一种具有核壳结构的改性纳米SiO2。借助傅立叶红外光谱(FT-IR)、激光粒度分析仪(PSDA)和透射电镜(TEM),表征了改性纳米SiO2的分子结构,并对比了其与未改性纳米SiO2在钻井液滤液中的粒度分布和微观形貌特征。通过模拟纳微米级孔隙地层封堵率测试实验,评价了不同纳米SiO2对纳微米微裂隙的封堵能力,并探讨了其在钻井液中纳米级分散作用机理。实验结果表明,改性纳米SiO2在钻井液中呈现纳米级分散,相比于未改性SiO2而言,可有效对纳微米裂隙进行封堵;当质量百分浓度为3.0%时,对模拟纳微米级地层的封堵率达到99.21%。Abstract: A modified nano SiO2 with core-shell structure was prepared through sol-gel method, using tetraethoxysilane (TEOS) as the source of Si, ammonia water as catalyst, water as accelerant, and phenylethylamine propyl trimethoxy silane as surface modifier. The molecular structure of the SiO2 was characterized through FT-IR, PSDA and TEM, and the modified SiO2 was compared with nonmodified SiO2 as to the particle size distribution and microscopic morphology in the filtrate of drilling fluid. Several nano SiO2 additives were evaluated by testing their capabilities to plug nano fractures on a simulator, and the mechanism of nano-dispersion of these SiO2 additives in drilling fluids was discussed. Compared to non-modified SiO2, the modified SiO2 shows nano-dispersion in drilling fluids, and can effectively plug the nano-sized fractures. At a concentration of 3.0%, 99.21%of the nano-sized fractures on the simulator were plugged.
-
Key words:
- Drilling fluid /
- Nano SiO2 /
- Silane coupling agent /
- Particle size distribution /
- Microscopic morphology
-
[1] 唐文泉. 泥页岩水化作用对井壁稳定性影响的研究[D]. 东营:中国石油大学(华东),2011. TANG Wenquan. Study on effects of shale hydration on wellbore stability[D].Dongying:China University of Petroleum,2011. [2] 朱国涛. 泥页岩井壁稳定性力学与化学耦合模型研究[D]. 西安:西安石油大学,2012. ZHU Guotao. Share wellbore stability in mechanical and chemical coupling model[D].Xi'an:Xi'an Shiyou University,2012. [3] 赵峰,唐洪明,孟英峰,等. 微观地质特征对硬脆性泥页岩井壁稳定性影响与对策研究[J]. 钻采工艺,2007,30(6):16-18.ZHAO Feng,TANG Hongming,MENG Yingfeng,et al. Study on the influence of microscopic geologic characteristics on wellbore stability of brittle shale[J]. Drilling & Production Technology,2007,30(6):16-18. [4] 王建华,鄢捷年,苏山林. 硬脆性泥页岩井壁稳定评价新方法[J]. 石油钻采工艺,2006,28(2):28-30.WANG Jianhua,YAN Jienian,SU Shanlin. New method for evaluating borehole stability in brittle shale[J]. Oil Drilling & Production Technology,2006,28(2):28-30. [5] OORT E V,HALE A H,MODY F K,et al. Transport in shales and the design of improved water based shale drilling fluids[R]. SPE 28309,1994. [6] 岳前升,李玉光,何保生,等. 涠洲12-1N 油田硬脆性泥页岩研究及钻井液技术对策[J]. 中国海上油气,2005,17(1):44-47.YUE Qiansheng,LI Yuguang,HE Baosheng,et al. Research on the hard brittle shale and drilling fluid type in WZ 12-1N oilfield[J]. China Offshore Oil and Gas,2005,17(1):44-47. [7] 邱正松,王伟吉,董兵强,等. 微纳米封堵技术研究及应用[J]. 钻井液与完井液,2015,32(2):6-10.QIU Zhengsong,WANG Weiji,DONG Bingqiang,et al. Study and application of micro-nano plugging technology[J]. Drilling Fluid & Completion Fluid,2015,32(2):6-10. [8] CHOI H,CHEN I W. Surface-modified silica colloid for diagnostic imaging [J]. Journal of Colloid and Interface Science,2003,258(2):435-437. [9] 王鹏程,柳松,刘梦溪. 单分散纳米二氧化硅的制备与分散性研究[J]. 无机盐工业,2011,43(2):40-43.WANG Pengcheng,LIU Song,LIU Mengxi. Study on preparation and dispersivity of monodisperse silica nanoparticles[J]. Inorganic Chemicals Industry,2011,43(2):40-43. [10] 潘洪波,汪存东,刘建新. 纳米二氧化硅制备工艺的研究[J]. 中国胶黏剂,2014,23(9):41-44.PAN Hongbo,WANG Cundong,LIU Jianxin. Study on preparation technology of nano-silicon dioxide[J]. China Adhesives,2014,23(9):41-44. [11] DENG G,MICHAEL A M,PAUL R,et al. Control of surface expression of function groups on silica particles[J]. Materials Science and Engineering,2000,11(2): 165-172. [12] 康长瑞,王玲玲. 纳米二氧化硅溶胶粒子的制备研究[J]. 信息记录材料,2012,13(3):8-10.KANG Changrui,WANG Lingling. Preparation study of nanosize silica sol[J]. Information Recording Materials,2012,13(3):8-10. [13] LAZARO A,GRIEND M C,BROUWERS H J H,et al. The influence of process conditions and Ostwald ripening on the specific surface area of olivine nanosilica[J]. Microporous and Mesoporous Materials,2013,181(15):254-261.
点击查看大图
计量
- 文章访问数: 629
- HTML全文浏览量: 124
- PDF下载量: 279
- 被引次数: 0