Study on Low Temperature Cementing Slurry
-
摘要: 针对煤层气层的低温固井以及深水表层套管固井中油井水泥早期强度发展缓慢的问题,通过将胶体SiO2、硫酸盐和醇胺类物质三元复配,开发出一种复合型无氯早强剂AA。研究了该早强剂不同加量对油井水泥的影响,采用XRD、SEM分析水泥水化产物和微观形貌,并结合早强剂中各组分作用,分析了它的作用机理。通过向水泥中加入减轻材料和配套外加剂,形成了一套密度为1.35~1.87 g/cm3的低温固井水泥浆体系。研究结果表明,早强剂AA可以加速水泥熟料C3S、C2S的水化反应进程,同时消耗水泥水化生成的Ca(OH)2,胶体SiO2可以与Ca(OH)2发生火山灰反应生成C-S-H凝胶,它可以填充水泥颗粒之间的微孔隙,显著提高水泥石早期强度;该低温固井水泥浆在30℃下的24 h抗压强度大于13 MPa,稠化时间在196~258 min之间,失水量为24 mL,游离液为0,流动度大于20 cm。此外,该水泥浆体系具有直角稠化、防气窜性能优异等优点。Abstract: A chlorine-free early-strength agent AA was developed by compounding colloidal SiO2, sulfate and alcohol amine. The development of AA is aimed at solving the troubles existed in cementing low temperature coalbed methane wells and cementing the surface hole section of deep water offshore wells. Effects of AA on the performance of oil well cement were studied. Using XRD and SEM, the hydrate of cement and the functioning mechanism of AA were analyzed. A 1.35-1.87 g/cm3 cement slurry suitable for low temperature well cementing was prepared using light weight material and other additives. Laboratory study shows that AA simultaneouslyaccelerates the hydration of cement clinkers C3S and C2S, and consumes the Ca(OH)2 produced. Pozzlanic reaction between SiO2 and Ca(OH)2 give birth to a C-S-H gel, which fills the pores and spaces formed by cement particles. Early strength of set cement is thus remarkably enhanced. This low temperature cement slurry has 24 h compressive strength of 13 MPa at 30℃, thickening time of 196-258 min, filter loss of 24 mL, free liquid of 0, and mobility greater than 20 cm. Other advantages of this cement slurry include short transient time and gas channeling prevention.
-
Key words:
- Cement slurry /
- Low temperature /
- Early strength agent /
- Well cementing /
- Coalbed methane
-
孙晓杰, 张维滨, 李建华, 等. 渤海海域低密度早强水泥浆的室内研究[J]. 钻井液与完井液, 2014, 31(3):72-74. Sun Xiaojie, Zhang Weibin, Li Jianhua, et al. Laboratory study on low density early strength cement slurry used in offshore Bohai[J]. Drilling Fluid & Completion Fluid, 2014, 31(3):72-74. 张海山, 王永松, 宫吉泽, 等. 海上增韧防窜固井水泥浆体系研究及应用[J]. 钻井液与完井液, 2015, 32(4):59-62. Zhang Haishan, Wang Yongsong, Gong Jize, et al. Study and application of toughness enhanced and anti-channeling cement slurry used in offshore well cementing[J]. Drilling Fluid & Completion Fluid, 2015, 32(4):59-62. 李早元, 周超, 刘威, 等. 低温短候凝水泥浆体系室内研究[J]. 石油钻探技术, 2012, 40(2):46-50. Li Zaoyuan, Zhou Chao, Liu Wei, et al. Laboratory study on the cement slurry system with short waiting on cement time at low temperature[J]. Petroleum Drilling Techniques, 2012, 40(2):46-50. 王瑞和, 王成文, 步玉环, 等. 深水固井技术研究进展[J]. 中国石油大学学报:自然科学版, 2008, 32(1):77-81. Wang Ruihe, Wang Chengwen, Bu Yuhuan, et al. Research development of deepwater cementing technique[J]. Journal of China University of Petroleum:Edition of Natural Science, 2008, 32(1):77-81. 王成文, 王瑞和, 陈二丁, 等. 锂盐早强剂改善油井水泥的低温性能及其作用机理[J]. 石油学报, 2011, 32(1):140-144. Wang Chengwen, Wang Ruihe, Chen Erding, et al. Performance and mechanism of the lithium salt accelerator in improving properties of the oil well cement under low temperature[J]. Acta Petrolei Sinica, 2011, 32(1):140-144. 张云理, 卞保芝. 混凝土外加剂产品及应用手册[M]. 中国铁道出版社, 1994, 129-135. Zhang Yunli, Bian Baozhi. Concrete admixture products and application manual[M]. China Railway Publishing House, 1994, 129-135. 王玉锁, 叶跃忠, 钟新樵, 等. 新型混凝土早强剂的应用研究现状[J]. 四川建筑, 2005, 25(4):105-106. Wang Yusuo, Ye Yuezhong, Zhong Xinqiao, et al. Present state of research on application of new concrete accelerators[J]. Sichuan Architecture, 2005, 25(4):105-106. 韩卫华, 佟刚, 杨红歧, 等. 一种新型油井水泥低温早强剂[J]. 钻井液与完井液, 2006, 23(3):31-33. Han Weihua, Tong Gang, Yang Hongqi, et al. A new low temperature high early strength cement for oil well[J]. Drilling Fluid & Completion Fluid, 2006,23(3):31-33. Hou P, Kawashima S, Kong D, et al. Modification effects of colloidal nanoSiO2 on cement hydration and its gel property[J]. Composites Part B:Engineering, 2013, 45(1):440-448. 叶青. 硅溶胶对水泥基材料微观结构和力学性能的影响[J]. 硅酸盐学报, 2008, 36(4):425-430. Ye Qing. Effect of silica sol dosage on mechanical properties and microstructure of cement-based material[J]. Journal of the Chinese Ceramic Society, 2008, 36(4):425-430. 韩松, 阎培渝, 刘仍光. 水泥早期水化产物的TEM研究[J]. 中国科学:技术科学, 2012, 42(8):879-885. Han Song, Yan Peiyu, Liu Rengguang.Study on the hydration product of cement in early age using TEM[J]. Science China Technological Sciences, 2012, 55(8):2284-2290. 姜梅芬,吕宪俊. 混凝土早强剂的研究与应用进展[J]. 硅酸盐通报, 2014, 33(10):2527-2533. Jiang Meifen, LYU Xianjun. Research and application progresses of concrete early strength agent[J]. Bulltin of the Chinese Ceramic Society, 2014, 33(10):2527-2533. Kontoleontos F, Tsakiridis P E, Marinos A, et al. Influence of colloidal nanosilica on ultrafine cement hydration:Physicochemical and microstructural characterization[J]. Construction and Building Materials, 2012, 35:347-360. SY/T 5480-1992注水泥流变性设计[S]. SY/T 5480-1992 Rheological design of cementing[S]. 徐伟祥, 王成文, 刘巍, 等. 新型抗高温粉煤灰低密度水泥浆[J]. 钻井液与完井液, 2015, 32(4):55-58. Xu Weixiang, Wang Chengwen, Liu Wei, et al. A new high temperature low density cement slurry with fly ash[J]. Drilling Fluid & Completion Fluid, 2015, 32(4):55-58. 张玉平, 杨远光, 宋元洪, 等. 超高温超高密度防气窜水泥浆[J]. 钻井液与完井液, 2015, 32(4):51-54. Zhang Yuping, Yang Yuanguang, Song Yuanhong, et al. Ultra high temperature and ultra high density cement slurry with gas-channeling[J]. Drilling Fluid & Completion Fluid, 2015, 32(4):51-54.
点击查看大图
计量
- 文章访问数: 766
- HTML全文浏览量: 154
- PDF下载量: 176
- 被引次数: 0