Study on Composite Polyelectrolyte Solution Used in Water Base Fracturing Fluid
-
摘要: 以物理交联为出发点,以聚电解质复合为基础,探讨聚电解质复合溶液作为压裂液稠化剂的可行性。实验发现调节阴、阳聚电解质的分子量和阳离子度等条件得到均相稳定的聚电解质复合物。分子量为80万和阳离子度为9.1%的阳离子聚合物与分子量为2200万的阴离子聚合物复合形成具有高黏弹性能的聚电解质复合物。聚电解质复合物溶液的电子扫描显微镜(SEM)表明,通过库伦力的作用而形成的聚电解质复合物形成网络结构,且不同状态的聚电解质复合物的网络结构不同。对可以作为压裂液增稠剂的聚电解质复合物溶液的流变分析表明,其具有良好的黏弹性能,在频率大于0.1 Hz时,储能模量远大于耗能模量。黏温曲线显示在170 s-1剪切速率下、130℃时,该聚电解质复合物溶液的黏度仍保持在40 mPa·s以上。实验现象表明均相聚电解质复合物有望形成一种新的超分子压裂液体系。Abstract: Composite polyelectrolyte solution is studied for its use in fracturing fluid as thickening agent.It was found that stable homogeneous composite polyelectrolyte can be obtained by adjusting the molecular weights of anionic and cationic polyelectrolytes, and the cationic degreeof cationic polyelectrolytes.A cationic polymer with molecular weight of 800, 000 and cationic degree of 9.1%, when mixed with an anionic polymer with molecular weight of 22, 000, 000, produces a composite polyelectrolyte with high viscoelasticity, Study of the composite polyelectrolyte with SEM shows that network structures are generated in polyelectrolyte formed through Coulomb force, and the network structures vary with different polyelectrolyte morphology.Analyses of the rheology of the solution of a composite polyclectrolyte used in fracturing fluids show that it has excellent viscoelasticity, and the storage modulus is far greater than the loss modulus at a frequency of 0.1 Hz.Viscosity- temperature curves show that at shear rate of 170 s-1 and 130℃, the composite polyelectrolyte solution still retain viscosity that is greater than 40 mPa·s.Homogeneous composite polyelectrolyte is expected to be used to prepare a new fracturing fluid system,
-
Key words:
- Composite polyelectrolyte /
- Water base fracturing fluid /
- SEM /
- Network structure
-
Evani S. Water-dispersible hydrophobic thickening agent:U.S. Patent 4,432,881[P].1984-2-21. 罗平亚,郭拥军,刘通义. 一种新型压裂液[J]. 石油与天然气地质,2007,28(4):511-515. Luo Pingya, Guo Yongjun, Liu Tongyi. A new type of fracturing fluid[J].Oil & Gas geology,2007,28(4):511-515. 李志臻, 杨旭, 夏冰, 等. 一种新型无瓜胶电吸引聚合物压裂液体系[J]. 钻井液与完井液,2014,31(5):85-88. Li Zhizhen, Yang Xu, Xia Bing,et al.Research and application of a new type of fracturing fluid without guar gum[J].Drilling Fluid & Completion Fluid,2014,31(5):85-88. Philipp B, Dautzenberg H, Linow K J, et al. Polyelectrolyte complexes-recent developments and open problems[J]. Progress in Polymer Science,1989,14(1):91-172. 董雯. 新型耐温抗盐聚合物增黏剂的合成及性能评价[J]. 西安石油大学学报:自然科学版,2014,29(5):75-79. Dong Wen. Synthesis and performance evaluation of a new polymer thickener resisting to high temperature and salt[J]. Journal of Xi'an Shiyou University(Natural Science), 2014, 29(5):75-79. 淡宜,王琪. 聚(丙烯酰胺-丙烯酸)/聚(丙烯酰胺-二甲基二烯丙基氯化铵)分子复合型聚合物驱油剂的增黏作用[J]. 高等学校化学学报,1997,18(5):818-822. Dan Yi,Wang Qi. Studies on viseosity enhancement of p(am-aa)/p(am-dmdaac) complex used as polymer flooding agent[J].Chemical Journal of Chinese Universities, 1997,18(5):818-822. 吴伟,高艳敏,张晓云. 一种高温嵌段聚合物水基压裂液的室内研究[J]. 钻井液与完井液,2010,27(1):68-70. Wu Wei, Gao Yanmin, Zhang Xiaoyun.Laboratory study of a high temperature block polymer water base fracturing fluid[J].Drilling Fluid & Completion Fluid,2010,27(1):68-70. 李志刚, 乌效鸣, 李子丰, 等. 低压低渗气藏低伤害压裂液研究与应用[J]. 钻井液与完井液, 2005, 22(3):34-37. Li Zhigang, Wu Xiaoming, Li Zifeng, et al.Premium N2 energized aqueous fracturing fluid for low-pressure and tight gas reservoir[J].Drilling Fluid & Completion Fluid,2005, 22(3):34-37. -
点击查看大图
计量
- 文章访问数: 707
- HTML全文浏览量: 147
- PDF下载量: 218
- 被引次数: 0
下载: