Synthesis and Performance of a High Temperature Filter Loss Reducer for Oil Well Cementing
-
摘要: 针对目前的AMPS共聚物固井降失水剂存在对水泥浆稠化时间影响大、耐高温能力差等问题,选择了具有特殊官能团的单体,以AMPS、N,N-二甲基丙烯酰胺(DMAA)、3-烯丙氧基-2-羟基-1-丙磺酸(AHPS)和AA为原料,合成了新型油井水泥降失水剂SCF,并通过红外光谱和热失重分析对共聚物的结构及耐热性能进行了表征。评价了添加降失水剂SCF的水泥浆综合性能。结果表明,加有3%~6% SCF的水泥浆API失水量可以控制在50 mL以下,抗温可达180℃;使水泥浆的稠化时间稍有延长,在100℃、加量为6%时,延长52 min,抗压强度略有降低,抗析水能力增强;其抗盐能力可达到36%。分析结果表明,该降失水剂靠改变滤饼的电性质和增加水泥浆体相黏度来实现对失水的控制。得出,该降失水剂合成工艺简单,综合性能良好,具有良好的应用前景。Abstract: A filter loss reducer for use in oil well cement slurries was synthesized with(AMPS), N, N-Dimethylacrylamide(DMAA), 3-Allyloxy-2-hydroxy-1-propanesulfonic acid(AHPS) and acryl acid(AA).Molecular structure and thermal stability of the copolymer were characterized using IR and TG.Laboratory evaluation of the copolymer showed that API filter loss of a cement slurry(3%-6%) can be reduced to less than 50 mL.The copolymer functioned well at 180℃ or under contamination of the cement slurry by 36% of salt.Laboratory evaluation shows that the filter loss reducer control filter loss by changing electrical porperties of filter cake and increasing viscosity of cement slurry.Thickening time of the cement slurry was also slightly prolonged.
-
Key words:
- Oil well cement /
- Filter loss reducer /
- High temperature tolerance /
- Synthesis
-
郭锦棠, 卢海川, 靳建州, 等. 新型耐温抗盐降失水剂的合成与测试[J]. 天津大学学报, 2012, 45(11):1001-1006. Guo Jintang,Lu Haichuan,Jin Jianzhou,et al. Synthesis and test of novel temperature-resistant and salt-tolerant fluid loss additive[J].Journal of Tianjin University,2012,45(11):1001-1006. 吕兴辉, 李燕, 常领, 等. 耐温抗盐聚合物水泥降失水剂的合成与性能评价[J]. 钻井液与完井液, 2010, 27(2):43-46. LYU Xinghui,Li Yan,Chang Ling,et al.The synthesisand properties evaluation of temperature-resistant and salttolerant polymeric cement fluid loss additive[J].Drilling Fluid & Completion Fluid,2010,27(2):43-46. 刘景丽,郝惠军,李秀妹,等. 油井水泥降失水剂接枝改性聚乙烯醇的研究[J]. 钻井液与完井液,2014,31(5):78-80. Liu Jingli, Hao Huijun, Li Xiumei, et al. Study on graft modified PVA-A cement slurry fluid loss reducer[J]. Drilling Fluid & Completion Fluid,2014,31(5):78-80. 王中华. 超高温钻井液体系研究(Ⅰ):抗高温钻井液处理剂设计思路[J]. 石油钻探技术,2009,37(3):1-7. Wang Zhonghua.The study of superhigh temperature drilling fluid(Ⅰ):The design method of temperatu reresistant drilling fluid[J].Petroleum Drilling Techniques,2009,37(3):1-7. Kelessidis V C,Tsamantaki C,Michalakis A,et al.Greek lignites as additives for controlling filtration properties of water-bentonite suspensions at high temperatures[J].The Science and Technology of Fuel and Energy,2007,86(11):1112-1121. Dugonjic-Bilic F,Plank J.High-temperature-resisting and salt-resisting spacer fluid contains fluid loss additive, suspension stabilizer,fluidity regulator,barite powder or iron ore powder,and pure water[J].Journal of Applied Polymer Science,2011,121(3):1262-1275. Holland BJ,Hay JN.The kinetics and mechanisms of the thermal degradation of poly(methyl methacrylate) studied by thermal analysis-Fourier transform infrared spectroscopy[J].Polymer,2011,42(11):4825-4835. -
点击查看大图
计量
- 文章访问数: 875
- HTML全文浏览量: 200
- PDF下载量: 194
- 被引次数: 0
下载: