Study and Evaluation of a Nano Compound Strength Enhancer
-
摘要: 低密度水泥浆体系常面临水泥石强度低、顶部强度发展缓慢的问题,而常规促凝早强材料虽可增加水泥石强度,但多会明显缩短稠化时间,稠化时间和强度之间矛盾突出。针对该问题,通过引入表面改性的纳米材料,搭配高效激活材料,开发出了一种“弱促凝、高早强”型复合增强剂。针对不同低密度水泥浆体系,通过控制增强剂加量、温度、水灰比、密度等变量,对该剂进行了评价实验。结果表明,纳米基复合增强剂可在对稠化时间影响较小的前提下,大幅提高水泥石的抗压强度,其中低密度水泥石顶部强度提高率可达40%以上,在不同类型低密度水泥浆体系中均有提强效果,并在长庆油田进行了应用,效果良好。Abstract: Set cement from a low-density cement slurry has low strength and slow hardness development at the top of the cement slurry. Regular accelerating early strength materials, though can be used to enhance the strength of the set cement, will obviously shorten the thickening time of the cement slurry, hence reducing the strength of the set cement. To solve this problem, a "weak accelerating high early strength" compound strength enhancer was developed with a surface modified nano material and some high efficiency activators. The strength enhancer was evaluated in different low-density cement slurries by controlling the concentration of the strength enhancer, temperature, water/cement ratio and density. It was found in the evaluation experiments that the strength enhancer can greatly increase the compressive strength of the set cement, with only minor effect on the thickening time of the cement slurry. In these experiments, the percent strength increase of the top of the low-density cement slurry can be 40% or higher. The nano compound strength enhancer can be used in different low-density cement slurries to improve the compressive strength of the set cement. Application of this strength enhancer in Changqing Oilfield has proved its good performance.
-
Key words:
- Low density cement slurry /
- Early strength agent /
- Nano material /
- Weakly accelerating
-
[1] SELVAM R P, SUBRAMANI V J, MURRAY S, et al. Potential application of nanotechnology on cement based materials[J]. Compressive Strength, 2009. [2] SATO T. Applications of nanotechnology for the sustainable development of cement-based materials[J]. University of Ottawa, 2006. [3] SANTRA A K, BOUL P, PANG X. Influence of nanomaterials in oilwell cement hydration and mechanical properties[M]. 2012. [4] LIU C, ZHU C, JIN L, et al. Exploratory investigation of nanomaterials to improve strength and permeability of concrete[J]. Transportation Research Record Journal of the Transportation Research Board, 2010, 2142(2142):1-8. [5] HUANG T, CREWS J B. Nanotechnology applications in viscoelastic surfactant stimulation fluids[M]. Society of Petroleum Engineers, 2008. [6] 杨昆鹏,项忠华,黄鸣宇,等. 低成本超低密度水泥浆体系研究与应用[J]. 钻井液与完井液,2018,35(4):92-96.YANG Kunpeng,XIANG Zhonghua,HUANG Mingyu,et al.Study and application of a low cost ultralow density cement slurry[J].Drilling Fluid & Completion Fluid,2018,35(4):92-96. [7] 刘景丽,彭松,王野,等. 二连盆地低阶煤层超低密度水泥浆固井技术[J]. 钻井液与完井液,2019,36(3):344-348.LIU Jingli, PENG Song, WANG Ye,et al.Cementing low-rank coal bed with ultra-low density cement slurry in Erlian basin[J].Drilling Fluid & Completion Fluid, 2019,36(3):344-348. [8] 王涛, 申峰, 展转盈, 等. 高强微弹水泥浆在延长油田致密油水平井中的应用[J]. 石油钻探技术, 2019, 47(5):40-48.WANG Tao, SHEN Feng, ZHAN Zhuanying, et al. The Application of High-Strength Micro-Elastic Cement Slurry in the Tight Oil Horizontal Wells of the Yanchang Oilfield[J]. Petroleum Drilling Techniques, 2019, 47(5):40-48. [9] 丁志伟,李嘉奇,赵靖影,等. 窄密度窗口正注反挤低密度水泥浆固井技术[J]. 钻井液与完井液,2019, 36(6):759-765.DING Zhiwei, LI Jiaqi, ZHAO Jingying,et al.Normal spotting and reverse squeezing of low-density cement slurries in wells with narrow safe drilling windows[J]. Drilling Fluid & Completion Fluid,2019,36(6):759-765. [10] 杨远光, 张继尹, 马思平. 油井水泥低温早强剂室内研究[J]. 西南石油大学学报(自然科学版), 2009,31(1):141-144. YANG Yuanguang,ZHANG Jiyin,MA Siping. Laboratory Study on Low Temperature Early Strength Agent of Oil Well Cement Slurry[J].Journal of Southwest Petroleum University(Science & Technology Edition), 2009,31(1):141-144. [11] 牟忠信, 张明昌, 李萍. 复合型早强剂水泥浆体系研究[J]. 西部探矿工程, 2005, 17(z1):135-137.MOU Zhongxin, ZHANG Mingchang, LI Ping.Research on cement slurry system of compound early strength agent[J].West-China Exploration Engineering,2005,17(z1):135-137. [12] 田野,符军放,宋维凯,等. 一种新型超深水低温早强剂[J]. 钻井液与完井液,2019,36(2):224-228.TIAN Ye, FU Junfang, SONG Weikai,et al.A new low temperature early strength agent for ultradeep water operation[J].Drilling Fluid & Completion Fluid,2019, 36(2):224-228. [13] 程小伟, 李宁, 滕学清, 等. 一种低密度水泥浆早强剂的制备方法:中国,CN201410280374.3[P].2014-09-10. CHENG Xiaowei, LI Ning, TENG Xueqing,et al. Preparation method of low-density cement slurry early strength agent:中国,CN201410280374.3[P].2014-09-10. [14] 张小伟, 肖瑞敏, 张雄. 粉煤灰矿粉水泥胶凝体系的高效复合早强剂研制[J]. 建筑材料学报, 2012, 15(2):249-254.ZHANG Xiaowei,XIAO Min,ZHANG Xiong. Preparation of high performance composites strength accelerator for cement containing fly ash and ground granulated blast-furnace slag[J].Journal of Building Materials,2012, 15(2):249-254.
点击查看大图
计量
- 文章访问数: 495
- HTML全文浏览量: 141
- PDF下载量: 81
- 被引次数: 0