A High Temperature Stabilizer for Set Cement
-
摘要: 针对普通加砂水泥石经受高温后抗压强度衰退的问题,研发出一种油井水泥石高温稳定剂,该稳定剂对水泥浆的稠化时间、水泥石常温强度发育、流变性无副作用,与油井水泥外加剂配伍性良好,形成的水泥石高温下(320℃、450℃)抗压强度不衰退,优于加砂水泥石及超细二氧化硅水泥石。同时加入高温稳定剂的水泥浆还具有很好的胶结强度,约是加砂水泥石环的4倍,超细二氧化硅水泥石环的3.5倍。该高温稳定剂在蒙古林油田现场应用2口井,整个施工过程顺利,固井质量较好,一二界面胶结质量良好,具有良好的应用前景。Abstract: A high temperature stabilizer has been developed for use in cement slurries to deal with decline of compressive strength of common set cement with sand at elevated temperatures. This stabilizer is well compatible with other additives in cement slurries and has no side effects on the thickening time and the development of the strength of the set cement at room temperatures. A set cement treated with this stabilizer had compressive strength that did not decline at elevated temperatures (320℃ and 450℃, respectively), showing better properties than set cement with sand and ultra-fine silica set cement. Cement slurries treated with this high temperature stabilizer had good cementation strength, which is 4 times of the cementation strength of cement sheath formed by cement slurries with sand, and 3.5 times of the cementation strength of the ultra-fine silica cement sheath. Operation of two wells with this high temperature stabilizer in Block Menggulin was successful and good well cementing job was performed, the cementation between the casing string and cement sheath as wells as the cementation between the cement sheath and the borehole wall were satisfactory, indicating that the high temperature stabilizer has good application prospect.
-
[1] 李早元, 伍鹏, 吴东奎, 等. 稠油热采井固井用铝酸盐水泥浆体系的研究及应用[J]. 钻井液与完井液, 2014, 31(5):71-74.LI Zaoyuan, WU Peng, WU Dongkui, et al. Research and application of aluminate cement slurry system for heavy oil thermal recovery cementing[J]. Drilling Fluid & Completion Fluid, 2014, 31(5):71-74. [2] 吴鹏. 辽河油田稠油热采井固井铝酸盐水泥体系研究[D]. 四川成都:西南石油大学, 2014. WU Peng. Research on cementing aluminate cement system of heavy oil thermal recovery wells in Liaohe Oilfield[D]. Sichuan Chengdu:Southwest Petroleum University, 2014. [3] 张弛, 陈小旭, 李长坤, 等. 抗高温硅酸盐水泥浆体系研究[J]. 钻井液与完井液, 2017, 34(5):62-66.ZHANG Chi, CHEN Xiaoxu, LI Changkun, et al. Study of high temperature silicate cement slurry[J]. Drilling Fluid & Completion Fluid, 2017, 34(5):62-66. [4] 彭志刚, 张健, 陈大钧, 等. 一种稠油热采井固井用高温强度稳定剂:中国, CN107760287A[P]. 2018-03-06. PENG Zhigang, ZHANG Jian, CHEN Dajun, et al. A high-temperature strength stabilizer for heavy oil thermal recovery well cementing:China, CN107760287A[P]. 2018-03-06. [5] 罗杨, 李仕勇. 一种稠油热采井的防衰退水泥浆:中国, CN107892906A[P].2018-04-10. LUO Yang, LI Shiyong. An anti-fading cement slurry for heavy oil thermal recovery wells:China, CN107892906A[P].2018-04-10. [6] 刘书杰, 许明标, 谢仁军等. 一种稠油热采井耐高温弹性固井水泥浆体系及其制备方法:中国, CN109250972A[P].2019-01-22. Liu Shujie, Xu Mingbiao, Xie Renjun, etc. A high temperature resistant elastic cementing slurry system for heavy oil thermal recovery wells and its preparation method:China, CN109250972A[P].2019-01-22. [7] 刘立华, 栾震, 陈梦玉, 等. 氢氧化铝阻燃剂的表面改性及在软质聚氯乙烯中的应用研究[J]. 首都师范大学学报, 2019, 40(2):37-41.LIU Lihua, LUAN Zhen, CHEN Mengyu, et al. Surface modification of aluminum hydroxide flame retardant and its application in soft PVC[J]. Journal of Capital Normal University, 2019, 40(2):37-41. [8] 刘湘华. 油井水泥浆高温悬浮稳定剂的开发及性能研究[J]. 钻井液与完井液, 2019, 36(5):605-609.LIU Xianghua. Development of and study on a high temperature suspension stabilizer for oil well cement slurries[J]. Drilling Fluid & Completion Fluid, 2019, 36(5):605-609.
点击查看大图
计量
- 文章访问数: 518
- HTML全文浏览量: 146
- PDF下载量: 98
- 被引次数: 0